Geomet 500 ®

lucio — Sat, 15 Feb 2014 23:13:58 +0000

A unique product for optimal friction and anticorrosion performance

GEOMET® 500 is applied to fasteners and many type of metallic parts to protect from corrosion, and it is used in many industries

• Thin dry-film, non-electrolytic, self-lubricated
• Water-based chemistry
• Passivated zinc and aluminium flakes in a binder, patented chemistry
• Metallic silver appareance

Characteristics and performance *

• Coefficient of friction: 0,15 ± 0,03 (ISO 16047)
• No topcoat required
• No hydrogen embrittlement
• Excellent assembly and multi-tightening behavior
• Good mechanical damage (test method D24 1312, USCAR 32) and chemical
(test VDA 621-412) resistance
• Performance maintained at elevated temperatures (up to 300°C)
• Paintable coating
• Electrical conductivity for most application
• Bimetallic compatibility with aluminum
• Application cost savings

High corrosion resistance*

Coating Weight Salt Spray Test (ISO 9227 / ASTM B117) Cyclic Test
Grade A > 24 g/m2 > 240 hours without white rust > 720 hours without red rust 25 cycles APGE
Grade B > 36 g/m2 > 240 hours without white rust > 1000 hours without red rust 6 cycles ACT 50 cycles APGE

* Results may vary depending on substrate, geometry of parts and type of application processes

Application process

GEOMET® 500 can be applied by Dip-Spin, Spray, Dip-Drain-Spin using bulk or rack

Health and Safety

• Aqueous dispersion
• Complies with REACh
• Complies with the 2000/53/CE and 2002/95/CE directives

Among our worldwide specifications

• PEUGEOT / CITROËN (B 15 3320)
• FIAT (Capitolato 9.57513)
• FORD (S447 & S448)
• INTERNATIONAL TRUCK (TMS 4523)
• IVECO (18-1101)
• JAGUAR CARS & LAND ROVER (ST JLR.50.5050)
• SCHNEIDER ELECTRIC (ABD 00048)
• SNCF / RATP (ST001-01)
• BOSCH (0 204 Y81 074 Code H)
• JOHN DEERE (LaN 930-11.4)

International standards

EN ISO 10683 – Fasteners: non-electrolytic zinc flake coatings
EN 13858 – non-electrolytic zinc flake coatings on iron and steel parts
ASTM F1136 / F1136 M – Zinc/Aluminum Corrosion Protective Coatings for Fasteners

Geomet 500 Pdf

Geomet 321 ®

lucio — Sat, 15 Feb 2014 23:12:53 +0000

The world’s choice for corrosion protection

GEOMET® 321 is applied to protect fasteners and many type of metallic parts from corrosion and is used in many industries. It can be combined with PLUS® DACROLUB® or GEOKOTE® topcoats to provide a very broad range of friction coefficients. It is the most widely used product in zinc flake technology.

• Thin dry-film, non-electrolytic
• Water-based chemistry
• Passivated zinc and aluminium flakes in a binder, patented chemistry
• Metallic silver appearance

Characterictics and performance*

• The coefficient of friction can be adjusted to targeted values ranging from 0.06 to 0.20 (ISO 16047) with NOF METAL COATING GROUP’s selected topcoats
• It can be used with or without topcoat
• No hydrogen embrittlement
• Excellent assembly and multi-tighteni ng behavior (with lubricated topcoat)
• Good mechanical damage (test method D24 1312, USCAR 32) and chemical (test VDA 621-412) resistance
• Performance maintained at elevated temperatures (up to 300°C)
• Paintable coating
• Electrical conductivity for most application processes
• Bimetallic compatibility with aluminum

High corrosion resistance*

Coating Weight Salt Spray Test (IS0 9227/ASTM B117) Cyclic Test
> 24 g/m2 > 240 hours without white rust > 720 hours without red rust
> 24 g/m2 + topcoat > 720 hours without red rust 4 cycles ACT 60 cycles GMW 14872 60 cycles SAE J2334
> 36 g/m2 > 1000 hours without red rust

*Results may vary depending on substrate, geometry of parts and type of application processes

Application process
GEOMET® 321 can be applied by Dip-Spin, Spray, Dip-Drain-Spin using bulk or rack

Health and Safety

• Aqueous dispersion
• Complies with REACh
• Complies with the 2000/53/CE and 2002/95/CE directives

Among our worldwide specifications

• BMW (GS 90010)
• CHRYSLER (PS-5873, PS-9666)
• DAIMLER (DBL 9440)
• FIAT (Capitolato 9.57513)
• FORD (S438)
• GENERAL MOTORS (GMW3359-GMW14)
• IVECO (18-1101)
• PORSCHE (PN 11011)
• RENAULT (01-71-002)
• RENAULT Trucks (01-71-4002)
• VOLKSWAGEN (TL245)
• VOLVO Cars (VCS 5737,29)
• ALSTOM (DTRF 150213)
• BOMBARDIER (BT/CE-WN30-02)
• CATERPILLAR (1E1675G)
• JOHN DEERE (JDM F13)
• KNORR BREMSE (N12005)

International standards

EN ISO 10683 – Fasteners: non-electrolytic zinc flake coatings
EN 13858 – Non-electrolytic zinc flake coatings on iron and steel parts
ASTM F1136 / F1136 M – Zinc/Aluminum Corrosion Protective Coatings for Fasteners

Geomet 321 Pdf

Geokote ®

lucio — Sat, 15 Feb 2014 22:52:15 +0000

The topcoat adapted to new requirements

Resistance to chemicals and abrasion, improved control of the friction coefficients are requirements increasingly demanded by markets. The combination of the GEOMET® coating with the GEOKOTE® topcoats can respond to new expectations in many industrial sectors.

Characteristics and performance

• Resistance to hydrochloric, phosphoric, sulfuric acids, automobile fluids and other chemical agents
• GEOKOTE® has proved its strong resistance to repetitive abrasions
• The black, clear or other shades of GEOKOTE® gives freedom from possible stick-slip problems when tightening (VDA 235-203)
• The GEOMET® / GEOKOTE® combination is particularly suited to fasteners since it provides them with optimal protection and assembly properties
• Salt Spray Test according to ISO 9227*
GEOMET® 321/500 + GEOKOTE® > 720 hours without red rust

Application processes

These water-based organic topcoats can be applied in one single thin coat by Dip-Spin, Spray,Dip-Drain-Spin using bulk or rack processes

Environmental safety

• Aqueous dispersion
• Complies with REACh
• Complies with the 2000/53/CE and 2002/95/CE directives

Among our worldwide specifications

• CHRYSLER
• FORD
• GENERAL MOTORS
• RENAULT
• AMERICAN AXLE
• ARVIN MERITOR
• DANA CORPORATION
• DELPHI
• MGI COUTIER
• SHIVANI
• GENERAL ELECTRIC
• GENERIC OFFSHORE COATINGS

Pdf Geokete

Geomet® 500

admin — Thu, 07 Jun 2012 16:58:20 +0000

A unique product for optimal friction and anticorrosion performance

GEOMET® 500 is used for protection against corrosion of fasteners and all metallic parts in all industrial sectors.

• Thin dry-film, non-electrolytic, self-lubricated
• Water-based chemistry
• Passivated zinc and aluminium flakes in a binder, patented chemistry
• Metallic silver appareance

Characteristics and performance*

High corrosion resistance*

Application process

GEOMET® 500 can be applied by Dip-Spin, Spray, Dip-Drain-Spin using bulk or rack

Health and Safety

• Aqueous dispersion
• Complies with REACh
• Complies with the 2000/53/CE and 2002/95/CE directives

Among our worldwide specifications

International standards

EN ISO 10683 – Fasteners: non-electrolytic zinc flake coatings
EN 13858 – non-electrolytic zinc flake coatings on iron and steel
parts
ASTM F1136 / F1136 M – Zinc/Aluminum Corrosion Protective
Coatings for Fasteners

Scarica il pdf del Geomet 500

Torque’n Tension®

lucio — Thu, 07 Jun 2012 15:16:46 +0000

Dacrolub®

lucio — Thu, 07 Jun 2012 15:16:29 +0000

Lubrication for challenging tightening operations

DACROLUB® 10 is an organic topcoat obtained from water-soluble compounds. It is applied over GEOMET® coatings, thus allowing to reduce and control the friction coefficient of threaded parts.
DACROLUB® 10 is available in three versions: clear, blue and green.
Its properties are the same whatever the colour.

Characteristics and performance*

• Dry lubrication film
• Friction coefficient: 0,08 – 0,14 on parts with GEOMET®
measured according to ISO 16047
• DACROLUB® 10 gives freedom from possible stick-slip problems when tightening
(VDA 235-203)
• Appearance: DACROLUB® 10L: clear
DACROLUB® 10B: blue
DACROLUB® 10G: green
• Salt Spray Test according to ISO 9227 :
No effect on the corrosion resistance of the GEOMET® base-coat
• The combination GEOMET® / DACROLUB® 10
is particularly suited to fasteners since it provides them with optimal protection and
assembly properties
• Being easy to apply, the coloured DACROLUB® 10 can be used for part
identification
• Competitive coating cost

Application process

DACROLUB® 10 is dip – spin in one single thin coat

Environmental safety

• Aqueous dispersion
• Complies with REACh
• Complies with the 2000/53/CE and 2002/95/CE directives

Main worldwide specifications

• DAIMLER (DBL 9440.43/.89)
• FIAT Group (Cap. 9.57513)
• VDA 235-203
• VW Group (TL245)

Scarica il pdf del Dacrolub

Protek®

lucio — Thu, 07 Jun 2012 15:16:00 +0000

Geoblack® M-ML

lucio — Thu, 07 Jun 2012 15:13:02 +0000

When anticorrosion becomes a design requirement

GEOBLACK® is the system that combines the proven performance of GEOMET® range products with the enriching appearance of a black topcoat.
PLUS® Black and GEOKOTE® Black product ranges offer many
possibilities to meet your requirements.

• Combination of a GEOMET®: 321, 500 or 720 basecoat and a black topcoat
• Thin dry-film, non-electrolytic
• Water-based chemistry
• Even, consistent black color

Characteristics and performance*

• Coefficient of friction adapted to your specific requirements:
0.13 ± 0.03 or 0.15 ± 0.03 (Please contact us as other ranges are available)
• No hydrogen embrittlement
• High corrosion resistance (up to 1000 hrs Salt Spray Test)
• Strong resistance to chemical attack (depending on the configuration). No
coating damage when in contact with automotive fluids including brake fluids
and wheel cleaning solutions

Systems approved for fasteners

• GEOBLACK® 500M: GEOMET® 500 + PLUS® Black 500 M
This system is approved by VOLVO
• GEOBLACK® ML: GEOMET 321 + PLUS® ML Black
This system is approved by IVECO, FIAT, FORD, DAIMLER, CHRYSLER &
GM. It is used in many other applications in automotive and non-automotive
industries.

Application process
GEOBLACK® can be applied by Dip-Spin, Spray, Dip-Drain-Spin using bulk or rack

Health and Safety

• Aqueous dispersion
• Complies with REACh
• Complies with the 2000/53/CE and 2002/95/CE directives

Main worldwide specifications

• CHRYSLER (PS-5873 BLACK)
• FIAT (9.57513)
• FORD (WSS-M21P39-A3, WSS-M21P49-A3)
• GM (GMW 3359)
• JAGUAR CARS & LAND ROVER (ST JLR.50.5050)
• JOHN DEERE (JDM F13)
• INTERNATIONAL TRUCK (TMS 4520)
• IVECO (18-1101)
• VOLVO Cars (VCS5737,19)
• VOLVO Trucks (STD 121-0003)
• BOSCH (0 204 Y81 074 Code G finition 6)
• SCHNEIDER Electric (ABD 00050)

International standards

EN ISO 10683 – Fasteners-non-electrolytically applied zinc-flake
coatings
EN 13858 – Non-electrolytically applied zinc-flake coatings on iron
or steel parts
ASTM F1136 / F1136 M – Zinc/Aluminum Corrosion Protective
Coatings for Fasteners

Scarica il pdf del Geomet

PLUS® XL, L, VL, ML, M, 10

admin — Fri, 25 Sep 2009 20:15:05 +0000

Worldwide trusted and proven performance

The PLUS® topcoats are dry lubricated sealers. Their application over GEOMET® coatings permits the friction coefficient control on threaded parts and increases their resistance to corrosion.
The controlled sacrificial corrosion protection mechanism of GEOMET® is improved further with the PLUS® topcoats.

Characteristics and performance*

• Friction coefficient on GEOMET® 321 base-coat (ISO 16047)
PLUS® XL : 0.06 – 0.09
PLUS® L : 0.08 – 0.14
PLUS® VL : 0.09 – 0.14
PLUS® ML : 0.10 – 0.16
PLUS® M : 0.12 – 0.18
PLUS® : 0.14 – 0.20
PLUS® 10 : not lubricated
• Appearance: matte metallic silver (clear topcoats)
• Salt Spray Test according to ISO 9227 / ASTM B117
GEOMET® 321/500 + PLUS® XL, L, VL, M, ML, 10 > 720 hours without red rust
(with a GEOMET® 321/500 coating weight > 24 g/m²)
• Increased field performance of parts
• Improved contact corrosion resistance (to magnesium, rubber, aluminum, etc)
• Excellent resistance to solvents, fuels and brake fluids (VDA 621 412)
• Competitive production cost

Application process

These water-based inorganic products can be applied by Dip-Spin, Spray, Dip-Drain-Spin, using bulk or rack

* I risultati possono variare secondo il substrato, la geometria dei pezzi e il tipo di processo d’applicazione

Health and Safety

• Aqueous dispersion
• Complies with REACh
• Complies with the 2000/53/CE and 2002/95/CE directives

Main worldwide specifications

• PLUS® XL : PSA (B15 3320)
RENAULT (on drawings)
CHRYSLER (PS 9666)
• PLUS® L : CHRYSLER (PS-5873)
FIAT (Cap. 9.57513)
GENERAL MOTORS (GMW14)
IVECO (18-1101)
CATERPILLAR (1E1675G)
JOHN DEERE (JDM F13)
• PLUS® VL : BMW (GS 90010)
DAIMLER (DBL 9440)
OPEL (GMW 3359)
PORSCHE (PTL 7529)
RENAULT TRUCKS (01.71.4002)
VOLKSWAGEN Group (TL 245)
• PLUS® ML : FIAT (Cap. 9.57513)
FORD (WX 100 S438)
GENERAL MOTORS (GMW 3359)
IVECO (18-1101)
• PLUS® M : FIAT (Cap. 9.57513)
IVECO (18-1101)
RENAULT (01-71-002)
RENAULT TRUCKS (01.71.4002)
• PLUS® 10 : HONDA
NISSAN
PORSCHE (PTL 7529)
SUZUKI
VOLKSWAGEN Group (TL245)

International standards

EN ISO 10683 – Fasteners: non-electrolytic zinc flake coatings
EN 13858 – Non-electrolytic zinc flake coatings on iron and steel parts

Scarica il pdf del Plus

GEOMET® 321

admin — Fri, 25 Sep 2009 17:08:11 +0000

GEOMET® 321 is applied to protect fasteners and many type of metallic parts from corrosion and is used in many industries. It can be combined with PLUS®, DACROLUB® or GEOKOTE® topcoats to provide a very broad range of friction coefficients. It is the most widely used product in zinc flake technology.

• Thin dry-film, non-electrolytic
• Water-based chemistry
• Passivated zinc and aluminium flakes in a binder, patented chemistry
• Metallic silver appearance

Characterictics and performance*

• The coefficient of friction can be adjusted to targeted values ranging from 0.06 to 0.20 (ISO 16047) with NOF METAL COATING GROUP’s selected topcoats
• It can be used with or without topcoat
• No hydrogen embrittlement
• Excellent assembly and multi-tightening behavior (with lubricated topcoat)
• Good mechanical damage (test method D24 1312, USCAR 32) and chemical (test VDA 621-412) resistance
• Performance maintained at elevated temperatures (up to 300°C)
• Paintable coating
• Electrical conductivity for most application processes
• Bimetallic compatibility with aluminum

High corrosion resistance*

Application process

GEOMET® 321 can be applied by Dip-Spin, Spray, Dip-Drain-Spin using bulk or rack

Health and Safety

• Aqueous dispersion
• Complies with REACh
• Complies with the 2000/53/CE and 2002/95/CE directives

Among our worldwide specifications

International standards

EN ISO 10683 – Fasteners: non-electrolytic zinc flake coatings
EN 13858 – Non-electrolytic zinc flake coatings on iron and steel parts
ASTM F1136 / F1136 M – Zinc/Aluminum Corrosion Protective
Coatings for Fasteners

Geomet 321 – scarica il pdf